| Welding flux for
Submerged-Arc Welding |
|
|
|
|
| Standards: |
EN 760 |
S A AB 1 67
AC H5 |
|
EN 756 |
S 35 2 AB S1
|
|
EN 756 |
S 42 3 AB S2
|
|
EN 756 |
S46 2 AB
S2Mo |
|
DIN 32 522 -
TS 5387 |
B AB 1 87 AC
10 | |
|
| Application and Properties: |
|
Agglomerated semi-basic
flux for welding carbon and low alloy steel in single or
multipass technique and single or multi wire
applications. The weld metal, produced in combination
with corresponding wire electrodes, offers good
mechanical properties also at low temperatures. Good
slag removal in fillet and groove welds. Suitable for
use in production of pressure vessel, boiler, tank, LPG
bottle, steel construction and in shipbuilding. Also
suitable for longitudinal and spiral welding of pipes
also in combination with Mo, Ni, Ti, B alloyed wires.
Basicity Index : 1.3 |
|
|
|
| All-Weld
Metal Analysis (typical values in %) : |
| OE-S1 |
0.03-0.06 |
0.6-1.0
|
0.1-0.5
|
<0.02
|
<0.025 |
- |
| OE-S2 |
0.03-0.05 |
1.0-1.6
|
0.2-0.6
|
<0.02
|
<0.025 |
- |
| OE-S2 Mo |
0.04-0.08 |
1.1-1.4
|
0.2-0.6
|
<0.02
|
<0.025 |
0.4-0.65
|
|
|
| Mechanical
Properties of All-Weld Metal (single values are typical
values): |
| OE-S1
|
AW /
KS |
>350 |
440-550 |
>22 |
>80 |
>27 |
-
|
| OE-S2
|
AW /
KS |
>420 |
510-650 |
>22 |
>100 |
>50 |
>27 |
| OE-S2
Mo |
AW /
KS |
>490 |
570-690 |
>22 |
>90 |
>27 |
- |
|
| AW : As welded |
|
| Redrying: at
350˚C for 2 hours to obtain max. 5 ml/100 gr diffisuble
hydrogen |
|
| Packing
& Order Information : |
|
|
|
| Type of
Current/Polarity/Welding Positions : |
| You can click on
the figure to see its explanation... |
|
|
|