| Welding flux for
Submerged-Arc Welding |
|
|
|
|
| Standards: |
EN 760 |
S A FB 2 53
AC | |
|
| Application and Properties: |
|
Agglomerated basic flux
for welding stainless steels, also Ti or Nb stabilized
types and duplex stainless steels. Suitable for
multipass welding in fillet welds, butt welds and weld
overlay. It allows high welding speeds on thin
thicknesses in single or multipass technique. Good slag
removal even when hot. Basicity Index : 2.2 |
|
|
|
| All-Weld
Metal Analysis (typical values in %) : |
| OE-308L |
<0.04
|
1-2 |
0.3-0.8
|
18-21
|
9-11 |
- |
- |
<0.35
|
- |
| OE-309L |
<0.04
|
1-2 |
0.3-0.8
|
22.5-24
|
12.5-14
|
- |
- |
<0.35
|
- |
| OE-316L |
<0.04
|
1-2 |
0.3-0.8
|
17.5-19.5 |
11-13
|
2-3 |
- |
<0.35
|
0.04-0.06 |
| OE-347 |
<0.08
|
1-2 |
0.3-0.8
|
18-21
|
9-11 |
- |
<1.0
|
<0.35
|
0.04-0.08 |
| LEXAL S |
<0.04
|
1.1-1.5
|
0.5-0.8
|
21.5-23.5 |
7.5-9.5
|
2.5-3.5
|
- |
- |
0.12-0.18 |
|
|
| Mechanical
Properties of All-Weld Metal (single values are typical
values): |
| OE-308L |
AW /
KS |
>340 |
>520 |
>35 |
- |
>50 |
| OE-309L |
AW /
KS |
>380 |
>520 |
>30 |
- |
>70 |
| OE-316L |
AW /
KS |
>440 |
>520 |
>30 |
- |
>40 |
| OE-347 |
AW /
KS |
>430 |
>520 |
>30 |
- |
>35 |
| LEXAL
S |
AW /
KS |
>570 |
>740 |
>26 |
>60 |
- |
|
|
|
| Redrying: at
350˚C for min. 2 hours |
|
| Type of
Current/Polarity/Welding Positions : |
| You can click on
the figure to see its explanation... |
|
|
|