| Basic tubular cored
electrode for MAG-Welding |
|
|
|
|
| Standards: |
EN 758 |
T 42 4 B C 3
H5 |
|
EN 758 |
T 42 4 B M 3
H5 |
|
DIN 8559
|
SG B1 CY
4254 |
|
AWS/ASME
SFA-5.20 |
E 70 T-5 H4
|
|
AWS/ASME
SFA-5.20 |
E 70 T-5 MJ
H4 | |
|
| Application and Properties: |
|
Basic type flux cored
(tubular) wire, producing weld metal of high mechanical
properties. Suitable for making very crack resistant and
tough welded joints, especially when welding steels
having higher carbon content. Easy slag removal and
pore-free welds. |
|
| Materials:
|
| S185 |
St 33 |
| S235 - S 355 |
St 37.0 - St 52.0
|
| S235 - S355 |
St 37-2 - St 52-3
|
| P235 - P355 |
St 37.4 - St 52.4
|
| E295, E335 |
St 50, St 60
|
| E360 |
St 70-2 |
| P235 |
St 35.8 |
| P265 |
St 45.8 |
| P235GH, P265GH |
HI, HII |
| P295GH, P355GH |
17 Mn 4, 19 Mn 5
|
| L210 - L360 |
StE 210.7 (TM) -
StE 360.7 (TM) |
| - |
A St 35, A St 52
|
| - |
StE 255 |
| S(P)275 - S(P)355
|
StE 285 - StE 355
|
| - |
X42, X46 |
| - |
A, B, D, E |
| - |
GS-48, GS-60
|
|
| Please observe
admissible operating temperatures for welding consumable
and base metal |
|
| All-Weld
Metal Analysis (typical values in %) : |
|
|
|
| Mechanical
Properties of All-Weld Metal (single values are typical
values): |
| SR/GS
|
>400 |
490-590 |
>22 |
>120 |
>80 |
>60 |
>47 |
| AW/KS
|
>420 |
510-610 |
>22 |
>120 |
>80 |
>60 |
>47 |
| N |
>280 |
420-520 |
>30 |
>160 |
- |
- |
- |
|
| AW : As welded, SR :
Stress relieved (2 hrs at 580°C/furnace cooling to
300°C) , N : Normalized (30 min 940°C/ air cooling)
|
|
| Chemical
compositions and mechanical properties apply to
the use of shielding gas |
|
: EN
439 - C1 (100% CO2) | |
|
| Shielding gas
as to EN 439 |
: C1 (100% CO2,
carbondioxide) | |
|
| Shielding gas
consumption |
: 12-15 l/min for
Ø< 1.60 mm, 15-20 l/min for Ø>2.0 mm
| |
|
| Packing
& Order Information : |
| 2043045 |
1.20 |
16 |
| 2043048 |
1.60 |
16 |
| 2043050 |
2.40 |
16 |
|
|
| Type of
Current/Polarity/Welding Positions : |
| You can click on
the figure to see its explanation... |
|
|
|