Covered electrode for Welding Stainless and Heat
Resisting Steels
|
| Basic Covering |
|
|
|
| Standards: |
EN 1600 |
E 13 4 B 42
|
|
DIN 8556
|
E 13 4 MPB
20 + |
|
AWS/ASME
SFA-5.4 |
E 410NiMo -
15 |
|
TS 2716
|
E 13 4 BS 20
|
|
TS 2716 EN
1600 |
E 13 4 B 42
| |
|
| Application and Properties: |
|
Basic type stainless
steel high recovery electrode, for welding of 12-14% Cr
and 3-4% Ni stainless and heat resistant chromium steels
or cast steels. Deposits martensitic stainless steel
weld metal. Also suitable for corrosion and abrasion
resistant surfacing welds (contact surfaces of gas,
water, sea water and steam fittings). Used with DCEP.
For wall thickness over 10 mm preheating to max. 150˚C
and after welding tempering or normalizing + tempering
are recommended. especially in joint welding a buffer
layer with E 106 or CITOCHROMAX electrode is
advisable. |
|
| Materials: |
| 1.4313 |
X 3 Cr Ni Mo 13 4 |
X 4 Cr Ni 13 4 |
- |
| 1.4313 |
G-X 6 Cr Ni 13 4 |
G-X 5 Cr Ni 13 4 |
CA 6-NM |
| 1.4407 |
- |
G-X 5 Cr Ni Mo 13 4 |
- |
| 1.4413 |
- |
X 3 Cr Ni Mo 13 4 |
- |
| 1.4414 |
- |
G-X 4 Cr Ni Mo 13 4 |
- |
|
| Please observe
admissible operating temperatures for welding consumable
and base metal |
|
| Qualification Tests |
: TSE
| |
|
| All-Weld Metal Analysis (typical
values in %) : |
| 0.06 |
0.50 |
0.80 |
12.0 |
4.00 |
0.5 |
|
|
| Mechanical Properties of
All-Weld Metal (single values are typical values): |
|
|
|
|
| Redrying: For
2 hrs. at 350°C. |
|
| Welding Current [A]: |
| 80-120 |
120-160 |
160-210 |
210-250 |
|
|
| Packing & Order Information
: |
| 1094010 |
2.50 |
350 |
190 |
3.76 |
4 |
15.05 |
| 1094016 |
3.25 |
350 |
115 |
3.84 |
4 |
15.36 |
| 1094020 |
4.00 |
350 |
100 |
5.15 |
4 |
20.60 |
| 1094028 |
5.00 |
350 |
25 |
2.63 |
4 |
10.53 |
|
|
| Type of Current/Polarity/Welding Positions
: |
| You can click on
the figure to see its explanation... |
|
|
|