Covered electrode for Welding Stainless and Heat
Resisting Steels
|
| Rutile Covering |
|
|
|
| Standards: |
EN 1600 |
E 18 8 Mn R
22 |
|
DIN 8556
|
E 18 8 Mn R
23 |
|
AWS/ASME
SFA-5.4 |
~E 307 - 16
|
|
TS 2716 EN
1600 |
E 18 8 Mn R
22 |
|
M.No.
|
1.4370
| |
|
| Application and Properties: |
|
High efficiency electrode
for joining dissimilar steels and depositing claddings
on ferritic steels. The weld metal consists of
austenitic Cr-Ni-Mo steel with possible small amounts of
delta ferrite. It is non-scaling up to +850°C. The weld
metal is highly crack resistant and therefore suited for
joining difficult to weld steels and depositing stress
relaxing buffer layers on crack sensitive base metal or
underneath hardfacing deposits. Weld metal work hardens.
Possible to use equally well both with AC and DC. High
current carrying capacity due to it's low alloy steel
core wire. Highest operating temperature for dissimilar
steel joints is +300°C. In the case of higher
temperatures, use CITONEL 600 electrodes. |
|
| Materials: |
| 1.3401 |
|
X 120 Mn 12 |
- |
| 1.4436 |
X 4 Cr Ni Mo 17 - 13 - 3 |
X 5 Cr Ni Mo 17 - 13 - 3 |
316 |
|
| Please observe
admissible operating temperatures for welding consumable
and base metal |
|
| All-Weld Metal Analysis (typical
values in %) : |
|
|
|
| Mechanical Properties of
All-Weld Metal (single values are typical values): |
|
|
| AW : As welded |
|
| Redrying: For
2 hrs. at 300°C. |
|
| Welding Current [A]: |
|
|
|
| Packing & Order Information
: |
| 1093208 |
2.50 |
300 |
60 |
1.03 |
9 |
9.29 |
| 1093214 |
3.25 |
300 |
62 |
1.75 |
9 |
15.79 |
| 1093220 |
4.00 |
350 |
40 |
2.21 |
9 |
19.87 |
| 1093228 |
5.00 |
350 |
25 |
2.00 |
9 |
17.96 |
|
|
| Type of Current/Polarity/Welding Positions
: |
| You can click on
the figure to see its explanation... |
|
|
|