Covered electrode for Welding Stainless and Heat
Resisting Steels
|
| Basic Covering |
|
|
|
| Standards: |
EN 1600 |
E 18 8 Mn B
22 |
|
DIN 8556
|
E 18 8 Mn B
20 |
|
AWS/ASME
SFA-5.4 |
~E 307 - 15
|
|
TS 2716
|
E 18 8 Mn B
20 |
|
TS 2716 EN
1600 |
E 18 8 Mn B
22 | |
|
| Application and Properties: |
|
Electrode particularly
designed for welding armour plates, dissimilar steels
and for surfacing purposes. The weld metal consists of
austenitic Cr-Ni-Mn stainless steel. It features high
resistance to cracking caused by impact and high
temperature and is therefore indicated for difficult to
weld steels and depositing stress relaxing buffer layers
on crack sensitive base metal or beneath hardfacing
deposits. Use with DCEP. No pre-heat or post welding
heat treatment is needed when welding armour plates.
Interpass temperature should not exceed 120°C. Shall be
used with shortest possible stick-out distance at 90°
angle to the work piece |
|
|
|
| Qualification Tests |
: TSE
| |
|
| All-Weld Metal Analysis (typical
values in %) : |
|
|
|
| Mechanical Properties of
All-Weld Metal (single values are typical values): |
|
|
| AW : As welded |
|
| Redrying: For
2 hrs. at 300°C. |
|
| Welding Current [A]: |
|
|
|
| Packing & Order Information
: |
| 1094816 |
3.25 |
300 |
60 |
1.70 |
6 |
10.22 |
| 1094820 |
4.00 |
350 |
50 |
2.17 |
6 |
12.99 |
| 1094828 |
5.00 |
350 |
30 |
2.00 |
9 |
18.04 |
|
|
| Type of Current/Polarity/Welding Positions
: |
| You can click on
the figure to see its explanation... |
|
|
|