Covered electrode for Welding Stainless and Heat
Resisting Steels
|
| Basic Covering |
|
|
|
| Standards: |
EN 1600 |
E 18 8 Mn B
22 |
|
DIN 8556
|
E 18 8 Mn B
20 |
|
AWS/ASME
SFA-5.4 |
~E 307 - 15
|
|
TS 2716
|
E 18 8 Mn B
20 |
|
TS 2716 EN
1600 |
E 18 8 Mn B
22 | |
|
| Application and Properties: |
|
Electrode for joining
dissimilar steels and depositing claddings on ferritic
steels. The weld metal consists of austenitic Cr-Ni-Mo
steel with possible small amounts of delta ferrite. It
is non-scaling up to +850°C. The weld metal is highly
crack resistant and therefore suited to joining
difficult to weld steels and depositing stress relaxing
buffer layers on crack sensitive base metal or
underneath hardfacing deposits. Weld metal work hardens.
Highest operating temperature for dissimilar steel
joints is +300°C. Use with DCEP. In the case of higher
temperatures, use CITONEL 600 electrodes. |
|
| Materials: |
| 1.3401 |
- |
X 120 Mn 12 |
- |
| 1.4436 |
X 4 Cr Ni Mo 17 - 13 - 3 |
X 5 Cr Ni Mo 17 - 13 - 3 |
316 |
|
| Please observe
admissible operating temperatures for welding consumable
and base metal |
|
| Qualification Tests |
: TSE
| |
|
| All-Weld Metal Analysis (typical
values in %) : |
|
|
|
| Mechanical Properties of
All-Weld Metal (single values are typical values): |
|
|
| AW : As welded |
|
| Redrying: For
2 hrs. at 300°C |
|
| Welding Current [A]: |
| 70-120 |
130-150 |
150-170 |
180-190 |
|
|
| Packing & Order Information
: |
| 1093008 |
2.50 |
300 |
60 |
1.08 |
9 |
9.72 |
| 1093014 |
3.25 |
300 |
60 |
1.78 |
9 |
16.04 |
| 1093020 |
4.00 |
350 |
40 |
2.13 |
9 |
19.19 |
| 1093028 |
5.00 |
350 |
25 |
2.00 |
9 |
17.96 |
|
|
| Type of Current/Polarity/Welding Positions
: |
| You can click on
the figure to see its explanation... |
|
|
|